Skip to product information
1 of 6

PayPal, credit cards. Download editable-PDF & invoice in 1 second!

GB/T 711-2017 English PDF (GBT711-2017)

GB/T 711-2017 English PDF (GBT711-2017)

Regular price $85.00 USD
Regular price Sale price $85.00 USD
Sale Sold out
Shipping calculated at checkout.
Quotation: In 1-minute, 24-hr self-service. Click here GB/T 711-2017 to get it for Purchase Approval, Bank TT...

GB/T 711-2017: Hot-rolled quality carbon structural steel plates sheets and strips

This Standard specifies the dimension, appearance, weight, technical requirements, test methods, inspection rules, package, marking and quality certificate of the hotrolled quality carbon structural steel plates sheets and strips. This Standard is only applicable to the hot-rolled quality carbon structural steel plates sheets and strips with thickness no greater than 100mm, width no less than 600mm (hereinafter referred to as steel sheets and strips).
GB/T 711-2017
GB
NATIONAL STANDARD OF THE
PEOPLE REPUBLIC OF CHINA
ICS 77.140.50
H 46
Replacing GB/T 711-2008, GB/T 710-2008
Hot-Rolled Quality Carbon
Structural Steel Plates Sheets and Strips
ISSUED ON. FEBRUARY 28, 2017
IMPLEMENTED ON. NOVEMBER 01, 2017
Issued by. General Administration of Quality Supervision, Inspection and Quarantine;
Standardization Administration of PRC.
Table of Contents
Foreword . 3
1 Scope .. 4
2 Normative References . 4
3 Ordering Contents . 6
4 Dimension, Appearance, Weight . 6
5 Technical Requirements .. 6
6 Test Methods . 12
7 Inspection Rules . 13
8 Package, Marking and Quality Certificate .. 14
Foreword
This Standard was drafted as per the rules specified in GB/T 1.1-2009.
This Standard combined and modified the following standards like GB/T 710-2008 Hot- Rolled Quality Carbon Structural Steel Sheets and Strips, GB/T 711-2008 Hot-rolled Quality Carbon Structural Steel Plates, Sheets and Wide Strips.
This Standard replaced GB/T 710-2008 Hot-Rolled Quality Carbon Structural Steel Sheets and Strips, GB/T 711-2008 Hot-rolled Quality Carbon Structural Steel Plates, Sheets and Wide Strips; compared with GB/T 710-2008 and GB/T 711-2008, this Standard has the major technical changes as follows.
--- Cancel the relevant brand of boiling steel;
--- Cancel the pull-edge level;
--- Increase three brands of 35Mn, 55Mn, 70Mn (see Table 1, Table 2, Table 3); --- Tighten the control harmful elemental sulfur in steel (see Table 1); --- Adjust the delivery status of some brands (see Table 2).
This Standard was proposed by China Iron and Steel Industry Association. This Standard shall be under the jurisdiction of National Technical Committee for Standardization of Steel (SAC/TC 183).
Drafting organizations of this Standard. Chongqing Iron and Steel Company Limited, Angang Steel Company Limited, China Metallurgical Information and Standardization Institute, Shougang Co., Ltd., Xinyu Iron and Steel Co., Ltd., and Hebei Iron and Steel Co., Ltd. Tangshan Branch.
Chief drafting staffs of this Standard. Du Dasong, Ye Guohua, Pu Zhimin, Zhang Weixu, Shi Li, Liao Sangsang, Deng Cuiqing, Xie Caozhong, Guan Jichun, Yang Juanyu, Gao Yan, Wang Xin, Liu Xuyuan, Su Haolu.
The historical editions replaced by this Standard are as follows.
--- GB/T 710-1998, GB/T 710-1991, GB/T 710-2008;
--- GB/T 711-1985, GB/T 711-1988, GB/T 711-2008.
Hot-Rolled Quality Carbon
Structural Steel Plates Sheets and Strips
1 Scope
This Standard specifies the dimension, appearance, weight, technical requirements, test methods, inspection rules, package, marking and quality certificate of the hot- rolled quality carbon structural steel plates sheets and strips.
This Standard is only applicable to the hot-rolled quality carbon structural steel plates sheets and strips with thickness no greater than 100mm, width no less than 600mm (hereinafter referred to as steel sheets and strips).
2 Normative References
The following documents are essential to the application of this document. For the dated documents, only the versions with the dates indicated are applicable to this document; for the undated documents, only the latest version (including all the amendments) are applicable to this document.
GB/T 222 Permissible Tolerances for Chemical Composition of Steel Products GB/T 223.5 Methods for Chemical Analysis of Iron, Steel and Alloy - The Reduced Molybdosilicate Spectrophotometric Method for The Determination of Acid-Soluble Silicon Content
GB/T 223.12 Methods for Chemical Analysis of Iron, Steel and Alloy - The Sodium Carbonate Separation-Diphenyl Carbazide Photometric Method for The
Determination of Chromium Content
GB/T 223.19 Methods for Chemical Analysis of iron, Steel and Alloy ?€? The Neocuproine-Chloroform Extraction Photometric Method for the Determination of Copper Content
GB/T 223.23 Methods for Chemical Analysis of Iron, Steel and Alloy - The Dimethylglyoxime Spectrophotometric Method for The Determination of Nickel Content
GB/T 223.37 Methods for Chemical Analysis of Iron, Steel and Alloy - The Indophenol Blue Photometric Method for the Determination of Nitrogen Content after Distillation Separation
GB/T 223.59 Iron, Steel and Alloy - Determination of Phosphorus Content - Bismuth Phosphomolybdate Blue Spectrophotometric Method and Antimony
Phosphomolybdate Blue Spectrophotometric Method
GB/T 223.64 Iron, Steel and Alloy - Determination of Manganese Content - Flame Atomic Absorption Spectrometric Method
GB/T 223.68 Methods for Chemical Analysis of Iron Steel and Alloy - The Combustion Potassium Iodate Volumetric Method for the Determination of Sulfur Content
GB/T 223.86 Steel and Iron - Determination of Total Carbon Content - Infrared Absorption Method after Combustion in an Induction Furnace
GB/T 224 Determination of Depth of Decarburization of Steels
GB/T 228.1 Metallic Materials - Tensile Testing - Part 1. Method of Test at Room Temperature
GB/T 229 Metallic Materials ?€? Charpy Notch Impact Test
GB/T 232 Metallic Materials ?€? Bend Test
GB/T 247 General Rule of Package Mark and Certification for Steel Plates (Sheets) and Strips
GB/T 709 Dimensions, Shape, Weight and Tolerances for Hot Rolled Steel Sheets and Strips
GB/T 2970 Thicker Steel Plate - Method for Ultrasonic Inspection
GB/T 2975 Steel and Steel Products - Location and Preparation of Test Pieces for Mechanical Testing
GB/T 4336 Carbon and Low-Alloy Steel - Determination of Multi-Element Contents -Spark Discharge Atomic Emission Spectrometric Method (Routine Method)
GB/T 6394 Metal - Methods for Estimating the Average Grain Size
GB/T 8170 Rules of Rounding off for Numerical Values and Expression and
Judgement of Limiting Values
GB/T 13298 Inspection Methods of Microstructure for Metals
GB/T 13299 Steel ?€? Determination of Microstructure
half thickness tolerance of steel plate and strip; the allowable minimum thickness of steel plate and strip must be guaranteed.
5.10.3 The local defects on the surface of the steel plate and strip are allowed to be cleaned; while the clean-up area shall be smooth and edge-free; the allowable minimum thickness of steel plate and strip must be guaranteed.
5.10.4 During the continuous production of steel strips, local surface defects are not easily found and removed; so, delivery with defects is allowed; however, the defective part shall not exceed 6% total length of each roll of steel strip.
5.10.5 Steel plate with thickness greater than 30mm is allowed for flame trimming; however, the steel plate requires the heat treatment shall take flame trimming before heat treatment.
5.10.6 The surface quality characteristics of each level of steel strip and shear steel plates shall conform to the provisions of Table 6.
Table 6 -- Surface Quality Characteristics of Each Level of Steel Plate and Strip Levels and
codes
Applicable surface
treatment modes Characteristics
Ordinary
surface (FA)
Rolled surface
Pickled surface
The surface is allowed to have pits, concaves, scratches,
and other slight and local defects of which the thickness (or
height) shall not exceed half thickness tolerance of the steel
strip; however, the allowable minimum thickness of steel
plate and strip must be guaranteed; the following local
defects are also allowed to have such as serrated edges,
partially uncut edges, lack of pickling, parking spots, etc.
Higher surface
(FB) Pickled surface
The surface is not allowed to have the local defects that may
influence the formability, such as slight scratches, slight
indentations, slight pits, slight roll marks, chromatic
aberration, etc.; the surface is allowed to have slight parking
spots after oiling; however, the surface is not allowed to have
the lack of or over pickling defects.
6 Test Methods
6.1 The analysis method for chemical compositions of steel shall be performed as per the provisions of GB/T 223.5, GB/T 223.12, GB/T 223.19, GB/T 223.23, GB/T 223.37, GB/T 223.59, GB/T 223.64, GB/T 223.68, GB/T 223.86, GB/T 4336, GB/T 20123, GB/T 20125, and general method; however, the arbitration shall be performed as per the provisions of GB/T 223.5, GB/T 223.12, GB/T 223.19, GB/T 223.23, GB/T 223.37, GB/T 223.59, GB/T 223.64, GB/T 223.68, GB/T 223.86.