GB/T 17394.4-2014 English PDF (GB/T17394.4-2014)

GB/T 17394.4-2014: Metallic materials - Leeb hardness test - Part 4: Tables of hardness values conversation
Delivery: 9 seconds. Download (& Email) true-PDF + Invoice.
Get Quotation: Click GB/T 17394.4-2014 (Self-service in 1-minute)
Historical versions (Master-website): GB/T 17394.4-2014
Preview True-PDF (Reload/Scroll-down if blank)

GB/T 17394.4-2014
GB
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 77.040.10
H 22
Metallic Materials – Leeb Hardness Test – Part 4: Tables of
Hardness Values Conversion
ISSUED ON: SEPTEMBER 30, 2014
IMPLEMENTED ON: MAY 01, 2015
Issued by: General Administration of Quality Supervision, Inspection and
Quarantine;
Standardization Administration of the People’s Republic of China.
Table of Contents
Foreword ... 3
1 Scope ... 4
2 Tables of Leeb Hardness Values Conversion for D-Type Impact Device ... 4
3 Tables of Leeb Hardness Values Conversion for G-Type Impact Device ... 16
4 Table of Leeb Hardness Values Conversion for C-type impact device ... 19
Foreword
GB/T 17394 Metallic Materials – Leeb Hardness Test consists of the following 4 parts:
--- Part 1: Test Method;
--- Part 2: Verification and Calibration of Hardness Tester;
--- Part 3: Calibration of Reference Blocks;
--- Part 4: Tables of Hardness Values Conversation.
This Part is Part 4 of GB/T 17394.
This Part was drafted as per the rules specified in GB/T 1.1-2009.
This Part was proposed by China Iron and Steel Industry Association.
This Part shall be under the jurisdiction of National Technical Committee on Steel of
Standardization Administration of China (SAC/TC 183).
Drafting organizations of this Part: Central Iron and Steel Research Institute; and China
Metallurgical Information and Standardization Institute.
Chief drafting staffs of this Part: Gao Yifei, and Dong Li.
Metallic Materials – Leeb Hardness Test – Part 4: Tables of
Hardness Values Conversion
1 Scope
This Part of GB/T 17394 gives the tables of Leeb hardness values conversion for D-type, G-
type and C-type impact devices.
2 Tables of Leeb Hardness Values Conversion for D-Type
Impact Device
For the tables of Leeb harness values conversion for D-type impact device made of carbon steel,
low-alloy steel and cast steel, cast iron, cast aluminum alloy, copper-zinc alloy, copper-
aluminum alloy and copper-tin alloy, pure copper and low-copper alloy, see Tables 1, 2, 3, 4, 5
and 6, respectively.
Table 1 -- Carbon Steel, Low Alloy Steel and Cast Steel (E≈210000 MPa)
GB/T 17394.4-2014
GB
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 77.040.10
H 22
Metallic Materials – Leeb Hardness Test – Part 4: Tables of
Hardness Values Conversion
ISSUED ON: SEPTEMBER 30, 2014
IMPLEMENTED ON: MAY 01, 2015
Issued by: General Administration of Quality Supervision, Inspection and
Quarantine;
Standardization Administration of the People’s Republic of China.
Table of Contents
Foreword ... 3
1 Scope ... 4
2 Tables of Leeb Hardness Values Conversion for D-Type Impact Device ... 4
3 Tables of Leeb Hardness Values Conversion for G-Type Impact Device ... 16
4 Table of Leeb Hardness Values Conversion for C-type impact device ... 19
Foreword
GB/T 17394 Metallic Materials – Leeb Hardness Test consists of the following 4 parts:
--- Part 1: Test Method;
--- Part 2: Verification and Calibration of Hardness Tester;
--- Part 3: Calibration of Reference Blocks;
--- Part 4: Tables of Hardness Values Conversation.
This Part is Part 4 of GB/T 17394.
This Part was drafted as per the rules specified in GB/T 1.1-2009.
This Part was proposed by China Iron and Steel Industry Association.
This Part shall be under the jurisdiction of National Technical Committee on Steel of
Standardization Administration of China (SAC/TC 183).
Drafting organizations of this Part: Central Iron and Steel Research Institute; and China
Metallurgical Information and Standardization Institute.
Chief drafting staffs of this Part: Gao Yifei, and Dong Li.
Metallic Materials – Leeb Hardness Test – Part 4: Tables of
Hardness Values Conversion
1 Scope
This Part of GB/T 17394 gives the tables of Leeb hardness values conversion for D-type, G-
type and C-type impact devices.
2 Tables of Leeb Hardness Values Conversion for D-Type
Impact Device
For the tables of Leeb harness values conversion for D-type impact device made of carbon steel,
low-alloy steel and cast steel, cast iron, cast aluminum alloy, copper-zinc alloy, copper-
aluminum alloy and copper-tin alloy, pure copper and low-copper alloy, see Tables 1, 2, 3, 4, 5
and 6, respectively.
Table 1 -- Carbon Steel, Low Alloy Steel and Cast Steel (E≈210000 MPa)