1
/
su
5
PayPal, credit cards. Download editable-PDF and invoice in 1 second!
GB/T 225-2006 English PDF (GBT225-2006)
GB/T 225-2006 English PDF (GBT225-2006)
Prezzo di listino
$85.00 USD
Prezzo di listino
Prezzo scontato
$85.00 USD
Prezzo unitario
/
per
Spese di spedizione calcolate al check-out.
Impossibile caricare la disponibilità di ritiro
Delivery: 3 seconds. Download true-PDF + Invoice.
Get QUOTATION in 1-minute: Click GB/T 225-2006
Historical versions: GB/T 225-2006
Preview True-PDF (Reload/Scroll if blank)
GB/T 225-2006: Steel -- Hardenability test by end quenching (Jominy test)
GB/T 225-2006
GB
NATIONAL STANDARD OF
THE PEOPLE’S REPUBLIC OF CHINA
ICS 77.040.99
H 24
GB/T 225-2006 / ISO 642.1999
Replacing GB/T 225-1988
Steel - Hardenability test by end quenching
(Jominy test)
(ISO 642.1999, IDT)
ISSUED ON. NOVEMBER 1, 2006
IMPLEMENTED ON. FEBRUARY 1, 2007
Issued by. General Administration of Quality Supervision, Inspection
and Quarantine;
Standardization Administration Committee.
Table of Contents
Foreword ... 3
1 Scope ... 5
2 Normative references ... 5
3 Principle... 6
4 Symbols and designations... 6
5 Form of test pieces and their preparation ... 6
6 Apparatus ... 9
7 Heating and quenching of test piece ... 11
8 Preparation for, and measurement of, hardness after quenching ... 12
9 Expression of results ... 14
10 Test report ... 15
Annex A (Informative) Specification for the hardenability of a product ... 17
Annex B (Normative) Additional information to clause 10 ... 20
Annex C (Informative) Calculation of the hardenability ... 22
Foreword
This Standard identically uses ISO 642.1999 Steel - Hardenability test by end
quenching (Jominy test).
For easy use, this Standard made the following editorial modifications to ISO
642.1999.
a) modified “this International Standard” to “this Standard”;
b) used “.” to replace “,” that was used as decimal point in ISO 642.1999;
c) used corresponding national standards to replace the references in ISO
642.1999;
d) deleted “Foreword” and “Bibliography” of ISO 642.1999;
e) redrew Figure 1.
This Standard replaces GB/T 225-1988 Steel - hardenability test by end
quenching (Jominy test).
Compared with GB/T 225-1988, the main modifications in this Standard are
as follows.
a) the standard name was modified from “Steel - hardenability test by end
quenching (Jominy test)” to “Steel - Hardenability test by end quenching
(Jominy test)”;
b) added “Foreword”;
c) the insulation time of test piece under heating temperature from (30 ± 5)
min to min (see Clause 4);
d) the cooling water temperature was modified from 10°C ~ 30°C to (20 ±
5)°C (see Clause 4);
e) the height of the water jet when no test piece is placed was modified
from (65 ± 5) mm to (65 ± 10) mm (see Clause 4);
f) the test piece blank size of machining sampling was modified from 30
mm to mm; the distance between test piece blank’s axis to
product surface was modified from (20 ± 5) mm to mm (5.1.2 b
of Edition 1988, 5.1 of this Edition);
g) the sampling method was modified FROM sampling method according
to test material size TO forging and machining; deleted 5.1.5 and 5.1.6
of GB/T 225-1988; added sampling provisions on continuous casting
products (see 5.1 of this Edition);
h) the insulation time at normalizing temperature was modified from 30 min
~ 60 min to min (5.2.3 of Edition 1988, 5.3 of this Edition);
i) deleted specific requirements for the roughness of the circumferential
and end faces of the test piece in Figure 2 (see Figure 2);
j) deleted the provisions on indentation point stagger arrangement; added
the provisions on indentation point position accuracy ±0.10 mm (8.3.1 b
of Edition 1988, 8.4.1.2 of this Edition);
k) self-tempering testing acid was modified to one type (8.1.3 of Edition
1988, 8.2 of this Edition);
l) Annex A of GB/T 225-1988 was adjusted to Annex B; added informative
Annex A, Annex C.
Annex A, Annex B and Annex C of this Standard are informative.
This Standard was proposed by China Iron and Steel Industry Association.
This Standard shall be under the jurisdiction of National Technical Committee
on Steel of Standardization Administration of China.
Main drafting organizations of this Standard. Baoshan Iron and Steel Co., Ltd.
Special Steel Branch, Metallurgical Industry Information Standards Institute,
Beijing Shougang Special Steel Co., Ltd., Iron and Steel Research Institute.
Main drafters of this Standard. Li Xiaodong, Luan Yan, Yu Xinxia, Wang
Guimin, Sun Shiqiu.
Versions of standard substituted by this Standard are.
- GB/T 225-1963, GB/T 225-1988.
Steel - Hardenability test by end quenching
(Jominy test)
1 Scope
This Standard specifies a method for determining the hardenability of steel by
end quenching (Jominy test) by using a test piece 25 mm in diameter and 100
mm long.
NOTE By agreement and for a defined field of application, the test described in this
Standard may be replaced by the calculation of the Jominy curve in accordance with an
accepted mathematical mode! (see annex C). In case of dispute, the test shall be earned
out.
2 Normative references
The following standards contain the provisions which, through reference in
this Standard, constitute the provisions of this Standard. For dated references,
subsequent amendments (excluding corrections) or revisions do not apply to
this Standard. However, the parties who enter into agreement based on this
Standard are encouraged to investigate whether the latest versions of these
documents are applicable. For undated reference documents, the latest
versions apply to this Standard.
GB/T 230.1, Metallic Rockwell hardness test - Part 1. Test method (scales
A, B, C, D, E, F, G, H, K, N, T) [GB/T 230.1-2004, ISO 6508-1.1999,
Metallic materials - Rockwell hardness test - Part 1. Test method (scales A,
B, C, D, E, F, G, K, N, T), MOD]
GB/T 230.2, Metallic Rockwell hardness test - Part2. Verification and
calibration of hardness testers (scales A, B, C, D, E, F, G, H, K, N, T) [GB/T
230.2-2002, ISO 6508-2.1999, Metallic materials - Rockwell hardness test
- Part 2. Verification and calibration of testing machines (scales A, B, C, D,
E, F, G, K, N, T), MOD]
GB/T 230.3, Metallic materials - Rockwell hardness test - Part 3.
Calibration of reference blocks (scales A, B, C, D, E, F, G, H, K, N, T)
[GB/T 230.3-2002, ISO 6508-3.1999, Metallic materials - Rockwell
hardness test - Part 3. Calibration of reference blocks (scales A, B, C, D, E,
F, G, K, N, T), MOD]
Get QUOTATION in 1-minute: Click GB/T 225-2006
Historical versions: GB/T 225-2006
Preview True-PDF (Reload/Scroll if blank)
GB/T 225-2006: Steel -- Hardenability test by end quenching (Jominy test)
GB/T 225-2006
GB
NATIONAL STANDARD OF
THE PEOPLE’S REPUBLIC OF CHINA
ICS 77.040.99
H 24
GB/T 225-2006 / ISO 642.1999
Replacing GB/T 225-1988
Steel - Hardenability test by end quenching
(Jominy test)
(ISO 642.1999, IDT)
ISSUED ON. NOVEMBER 1, 2006
IMPLEMENTED ON. FEBRUARY 1, 2007
Issued by. General Administration of Quality Supervision, Inspection
and Quarantine;
Standardization Administration Committee.
Table of Contents
Foreword ... 3
1 Scope ... 5
2 Normative references ... 5
3 Principle... 6
4 Symbols and designations... 6
5 Form of test pieces and their preparation ... 6
6 Apparatus ... 9
7 Heating and quenching of test piece ... 11
8 Preparation for, and measurement of, hardness after quenching ... 12
9 Expression of results ... 14
10 Test report ... 15
Annex A (Informative) Specification for the hardenability of a product ... 17
Annex B (Normative) Additional information to clause 10 ... 20
Annex C (Informative) Calculation of the hardenability ... 22
Foreword
This Standard identically uses ISO 642.1999 Steel - Hardenability test by end
quenching (Jominy test).
For easy use, this Standard made the following editorial modifications to ISO
642.1999.
a) modified “this International Standard” to “this Standard”;
b) used “.” to replace “,” that was used as decimal point in ISO 642.1999;
c) used corresponding national standards to replace the references in ISO
642.1999;
d) deleted “Foreword” and “Bibliography” of ISO 642.1999;
e) redrew Figure 1.
This Standard replaces GB/T 225-1988 Steel - hardenability test by end
quenching (Jominy test).
Compared with GB/T 225-1988, the main modifications in this Standard are
as follows.
a) the standard name was modified from “Steel - hardenability test by end
quenching (Jominy test)” to “Steel - Hardenability test by end quenching
(Jominy test)”;
b) added “Foreword”;
c) the insulation time of test piece under heating temperature from (30 ± 5)
min to min (see Clause 4);
d) the cooling water temperature was modified from 10°C ~ 30°C to (20 ±
5)°C (see Clause 4);
e) the height of the water jet when no test piece is placed was modified
from (65 ± 5) mm to (65 ± 10) mm (see Clause 4);
f) the test piece blank size of machining sampling was modified from 30
mm to mm; the distance between test piece blank’s axis to
product surface was modified from (20 ± 5) mm to mm (5.1.2 b
of Edition 1988, 5.1 of this Edition);
g) the sampling method was modified FROM sampling method according
to test material size TO forging and machining; deleted 5.1.5 and 5.1.6
of GB/T 225-1988; added sampling provisions on continuous casting
products (see 5.1 of this Edition);
h) the insulation time at normalizing temperature was modified from 30 min
~ 60 min to min (5.2.3 of Edition 1988, 5.3 of this Edition);
i) deleted specific requirements for the roughness of the circumferential
and end faces of the test piece in Figure 2 (see Figure 2);
j) deleted the provisions on indentation point stagger arrangement; added
the provisions on indentation point position accuracy ±0.10 mm (8.3.1 b
of Edition 1988, 8.4.1.2 of this Edition);
k) self-tempering testing acid was modified to one type (8.1.3 of Edition
1988, 8.2 of this Edition);
l) Annex A of GB/T 225-1988 was adjusted to Annex B; added informative
Annex A, Annex C.
Annex A, Annex B and Annex C of this Standard are informative.
This Standard was proposed by China Iron and Steel Industry Association.
This Standard shall be under the jurisdiction of National Technical Committee
on Steel of Standardization Administration of China.
Main drafting organizations of this Standard. Baoshan Iron and Steel Co., Ltd.
Special Steel Branch, Metallurgical Industry Information Standards Institute,
Beijing Shougang Special Steel Co., Ltd., Iron and Steel Research Institute.
Main drafters of this Standard. Li Xiaodong, Luan Yan, Yu Xinxia, Wang
Guimin, Sun Shiqiu.
Versions of standard substituted by this Standard are.
- GB/T 225-1963, GB/T 225-1988.
Steel - Hardenability test by end quenching
(Jominy test)
1 Scope
This Standard specifies a method for determining the hardenability of steel by
end quenching (Jominy test) by using a test piece 25 mm in diameter and 100
mm long.
NOTE By agreement and for a defined field of application, the test described in this
Standard may be replaced by the calculation of the Jominy curve in accordance with an
accepted mathematical mode! (see annex C). In case of dispute, the test shall be earned
out.
2 Normative references
The following standards contain the provisions which, through reference in
this Standard, constitute the provisions of this Standard. For dated references,
subsequent amendments (excluding corrections) or revisions do not apply to
this Standard. However, the parties who enter into agreement based on this
Standard are encouraged to investigate whether the latest versions of these
documents are applicable. For undated reference documents, the latest
versions apply to this Standard.
GB/T 230.1, Metallic Rockwell hardness test - Part 1. Test method (scales
A, B, C, D, E, F, G, H, K, N, T) [GB/T 230.1-2004, ISO 6508-1.1999,
Metallic materials - Rockwell hardness test - Part 1. Test method (scales A,
B, C, D, E, F, G, K, N, T), MOD]
GB/T 230.2, Metallic Rockwell hardness test - Part2. Verification and
calibration of hardness testers (scales A, B, C, D, E, F, G, H, K, N, T) [GB/T
230.2-2002, ISO 6508-2.1999, Metallic materials - Rockwell hardness test
- Part 2. Verification and calibration of testing machines (scales A, B, C, D,
E, F, G, K, N, T), MOD]
GB/T 230.3, Metallic materials - Rockwell hardness test - Part 3.
Calibration of reference blocks (scales A, B, C, D, E, F, G, H, K, N, T)
[GB/T 230.3-2002, ISO 6508-3.1999, Metallic materials - Rockwell
hardness test - Part 3. Calibration of reference blocks (scales A, B, C, D, E,
F, G, K, N, T), MOD]
Share