1
/
von
7
PayPal, credit cards. Download editable-PDF and invoice in 1 second!
GB/T 20564.6-2022 English PDF (GBT20564.6-2022)
GB/T 20564.6-2022 English PDF (GBT20564.6-2022)
Normaler Preis
$165.00 USD
Normaler Preis
Verkaufspreis
$165.00 USD
Grundpreis
/
pro
Versand wird beim Checkout berechnet
Verfügbarkeit für Abholungen konnte nicht geladen werden
Delivery: 3 seconds. Download true-PDF + Invoice.
Get QUOTATION in 1-minute: Click GB/T 20564.6-2022
Historical versions: GB/T 20564.6-2022
Preview True-PDF (Reload/Scroll if blank)
GB/T 20564.6-2022: Continuously cold rolled high strength steel sheet and strip for automobile - Part 6: Transformation induced plasticity steel
GB/T 20564.6-2022
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 77.140.50
CCS H 46
Replacing GB/T 20564.6-2010
Continuously Cold Rolled High Strength Steel Sheet and
Strip for Automobile - Part 6.Transformation Induced
Plasticity Steel
ISSUED ON. JULY 11, 2022
IMPLEMENTED ON. FEBRUARY 1, 2023
Issued by. State Administration for Market Regulation;
Standardization Administration of the People’s Republic of China.
Table of Contents
Foreword... 3
Introduction... 5
1 Scope... 7
2 Normative References... 7
3 Terms and Definitions... 9
4 Classification and Designation Expression Method... 9
5 Order Content... 10
6 Dimensions, Shapes and Weights... 11
7 Technical Requirements... 11
8 Test Methods... 14
9 Inspection Rules... 15
10 Packaging, Marking and Quality Certificate... 15
11 Comparison of Similar Designations in China and Foreign Countries... 15
Appendix A (informative) Reference Values of Chemical Composition (melting
analysis) of Steel Sheet and Strip... 16
Appendix B (informative) Comparison of Similar Designations in China and Foreign
Countries... 17
Bibliography... 18
Continuously Cold Rolled High Strength Steel Sheet and
Strip for Automobile - Part 6.Transformation Induced
Plasticity Steel
1 Scope
This document specifies the classification and designation expression method, order contents,
dimensions, shapes, weights, technical requirements, test methods, inspection rules, packaging,
marking and quality certificate of continuously cold rolled transformation induced plasticity
high strength steel sheet and strip for automobile.
This document is applicable to continuously cold rolled transformation induced plasticity high
strength steel sheet and strip (with a thickness of 0.50 mm ~ 2.5 mm) mainly used to fabricate
structural parts and reinforcements of automobile (hereinafter referred to as “the steel sheet and
strip”).
2 Normative References
The contents of the following documents constitute indispensable clauses of this document
through the normative references in this text. In terms of references with a specified date, only
versions with a specified date are applicable to this document. In terms of references without a
specified date, the latest version (including all the modifications) is applicable to this document.
GB/T 223.9 Iron, Steel and Alloy - Determination of Aluminum Content - Chrome Azurol S
Photometric Method
GB/T 223.12 Methods for Chemical Analysis of Iron, Steel and Alloy - The Sodium Carbonate
Separation-diphenyl Carbazide Photometric Method for the Determination of Chromium
Content
GB/T 223.23 Iron, Steel and Alloy - Determination of Nickel Content - The Dimethylglyoxime
Spectrophotometric Method
GB/T 223.26 Iron, Steel and Alloy - Determination of Molybdenum Content - The Thiocyanate
Spectrophotometric Method
GB/T 223.53 Methods for Chemical Analysis of Iron, Steel and Alloy - The Flame Atomic
Absorption Spectrophotometric Method for the Determination of Copper Content
GB/T 223.54 Methods for Chemical Analysis of Iron, Steel and Alloy - The Flame Atomic
Absorption Spectrophotometric Method for the Determination of Nickel Content
GB/T 223.59 Iron, Steel and Alloy - Determination of Phosphorus Content - Bismuth
Phosphomolybdate Blue Spectrophotometric Method and Antimony Phosphomolybdate Blue
Spectrophotometric Method
GB/T 223.60 Methods for Chemical Analysis of Iron, Steel and Alloy - The Perchloric Acid
Dehydration Gravimetric Method for the Determination of Silicon Content
GB/T 223.63 Iron, Steel and Alloy - Determination of Manganese Content - Sodium (potassium)
Periodate Spectrophotometric Method
GB/T 223.64 Iron, Steel and Alloy - Determination of Manganese Content - Flame Atomic
Absorption Spectrometric Method
GB/T 223.85 Steel and Iron - Determination of Sulfur Content - Infrared Absorption Method
after Combustion in an Induction Furnace
GB/T 223.86 Steel and Iron - Determination of Total Carbon Content - Infrared Absorption
Method after Combustion in an Induction Furnace
GB/T 228.1-2021 Metallic Materials - Tensile Testing - Part 1.Method of Test at Room
Temperature
GB/T 247 General Rule of Acceptance, Package, Mark and Certification for Steel Plates (sheets)
and Strips
GB/T 708 Dimension, Shape, Weight and Tolerance for Cold-rolled Steel Strip and Sheet
GB/T 2523 Measuring Method of Surface Roughness, Peak Count and Waviness for Cold-
rolled Metal Sheet and Strip
GB/T 2975 Steel and Steel Products - Location and Preparation of Samples and Test Pieces for
Mechanical Testing
GB/T 4336 Carbon and Low-alloy Steel - Determination of Multi-element Contents - Spark
Discharge Atomic Emission Spectrometric Method (routine method)
GB/T 5028 Metallic Materials - Sheet and Strip - Determination of Tensile Strain Hardening
Exponent
GB/T 8170 Rules of Rounding off for Numerical Values and Expression and Judgement of
Limiting Values
GB/T 17505 Steel and Steel Products - General Technical Delivery Requirements
GB/T 18253-2018 Steel and Steel Products - Types of Inspection Documents
GB/T 20066 Steel and Iron - Sampling and Preparation of Samples for the Determination of
Chemical Composition
GB/T 20123 Steel and Iron - Determination of Total Carbon and Sulfur Content Infrared
Absorption Method after Combustion in an Induction Furnace (routine method)
GB/T 20125 Low-alloy Steel - Determination of Multi-element Contents - Inductively Coupled
Plasma Atomic Emission Spectrometric Method
3 Terms and Definitions
The following terms and definitions are applicable to this document.
3.1 Transformation Induced Plasticity Steel; TR
Transformation induced plasticity steel refers to a type of steel whose microstructure is mainly
ferrite, bainite and retained austenite, and during the forming process, the retained austenite
may be transformed into a martensitic structure.
NOTE. transformation induced plasticity steel has a relatively high work hardening rate, uniform
elongation and tensile strength. In comparison with dual phase steel with equivalent tensile
strength, transformation induced plasticity steel has a higher elongation.
4 Classification and Designation Expression Method
4.1 Designation Expression Method
The designation of the steel sheet and strip is composed of three parts. the initials “CR” of the
English “Cold Rolled”, the specified minimum yield strength value / specified minimum tensile
strength value, and the first two letters “TR” of the English “Transformation Induced Plasticity”.
Example. CR380/590TR, in which.
CR---the initials of the English “Cold Rolled”;
380/590---380.the specified minimum yield strength value, 590.the specified minimum tensile strength
value, expressed in (MPa);
TR---the first two letters of the English “Transformation Induced Plasticity”.
4.2 Classification
4.2.1 The designations and recommended purposes of the steel sheet and strip are shown in
Table 1.
d) Specifications, dimensions and unevenness accuracy;
e) Surface quality level;
f) Surface structure;
g) Edge state;
h) Packaging mode;
i) Weight;
j) Purposes;
k) Other special requirements.
5.2 If the dimensions, unevenness accuracy, surface quality level, surface structure type, edge
state and packaging are not specified in the order contract, then, the products in this document
shall be delivered with ordinary dimensions and unevenness accuracy, and a relatively advanced
surface as tr...
Get QUOTATION in 1-minute: Click GB/T 20564.6-2022
Historical versions: GB/T 20564.6-2022
Preview True-PDF (Reload/Scroll if blank)
GB/T 20564.6-2022: Continuously cold rolled high strength steel sheet and strip for automobile - Part 6: Transformation induced plasticity steel
GB/T 20564.6-2022
NATIONAL STANDARD OF THE
PEOPLE’S REPUBLIC OF CHINA
ICS 77.140.50
CCS H 46
Replacing GB/T 20564.6-2010
Continuously Cold Rolled High Strength Steel Sheet and
Strip for Automobile - Part 6.Transformation Induced
Plasticity Steel
ISSUED ON. JULY 11, 2022
IMPLEMENTED ON. FEBRUARY 1, 2023
Issued by. State Administration for Market Regulation;
Standardization Administration of the People’s Republic of China.
Table of Contents
Foreword... 3
Introduction... 5
1 Scope... 7
2 Normative References... 7
3 Terms and Definitions... 9
4 Classification and Designation Expression Method... 9
5 Order Content... 10
6 Dimensions, Shapes and Weights... 11
7 Technical Requirements... 11
8 Test Methods... 14
9 Inspection Rules... 15
10 Packaging, Marking and Quality Certificate... 15
11 Comparison of Similar Designations in China and Foreign Countries... 15
Appendix A (informative) Reference Values of Chemical Composition (melting
analysis) of Steel Sheet and Strip... 16
Appendix B (informative) Comparison of Similar Designations in China and Foreign
Countries... 17
Bibliography... 18
Continuously Cold Rolled High Strength Steel Sheet and
Strip for Automobile - Part 6.Transformation Induced
Plasticity Steel
1 Scope
This document specifies the classification and designation expression method, order contents,
dimensions, shapes, weights, technical requirements, test methods, inspection rules, packaging,
marking and quality certificate of continuously cold rolled transformation induced plasticity
high strength steel sheet and strip for automobile.
This document is applicable to continuously cold rolled transformation induced plasticity high
strength steel sheet and strip (with a thickness of 0.50 mm ~ 2.5 mm) mainly used to fabricate
structural parts and reinforcements of automobile (hereinafter referred to as “the steel sheet and
strip”).
2 Normative References
The contents of the following documents constitute indispensable clauses of this document
through the normative references in this text. In terms of references with a specified date, only
versions with a specified date are applicable to this document. In terms of references without a
specified date, the latest version (including all the modifications) is applicable to this document.
GB/T 223.9 Iron, Steel and Alloy - Determination of Aluminum Content - Chrome Azurol S
Photometric Method
GB/T 223.12 Methods for Chemical Analysis of Iron, Steel and Alloy - The Sodium Carbonate
Separation-diphenyl Carbazide Photometric Method for the Determination of Chromium
Content
GB/T 223.23 Iron, Steel and Alloy - Determination of Nickel Content - The Dimethylglyoxime
Spectrophotometric Method
GB/T 223.26 Iron, Steel and Alloy - Determination of Molybdenum Content - The Thiocyanate
Spectrophotometric Method
GB/T 223.53 Methods for Chemical Analysis of Iron, Steel and Alloy - The Flame Atomic
Absorption Spectrophotometric Method for the Determination of Copper Content
GB/T 223.54 Methods for Chemical Analysis of Iron, Steel and Alloy - The Flame Atomic
Absorption Spectrophotometric Method for the Determination of Nickel Content
GB/T 223.59 Iron, Steel and Alloy - Determination of Phosphorus Content - Bismuth
Phosphomolybdate Blue Spectrophotometric Method and Antimony Phosphomolybdate Blue
Spectrophotometric Method
GB/T 223.60 Methods for Chemical Analysis of Iron, Steel and Alloy - The Perchloric Acid
Dehydration Gravimetric Method for the Determination of Silicon Content
GB/T 223.63 Iron, Steel and Alloy - Determination of Manganese Content - Sodium (potassium)
Periodate Spectrophotometric Method
GB/T 223.64 Iron, Steel and Alloy - Determination of Manganese Content - Flame Atomic
Absorption Spectrometric Method
GB/T 223.85 Steel and Iron - Determination of Sulfur Content - Infrared Absorption Method
after Combustion in an Induction Furnace
GB/T 223.86 Steel and Iron - Determination of Total Carbon Content - Infrared Absorption
Method after Combustion in an Induction Furnace
GB/T 228.1-2021 Metallic Materials - Tensile Testing - Part 1.Method of Test at Room
Temperature
GB/T 247 General Rule of Acceptance, Package, Mark and Certification for Steel Plates (sheets)
and Strips
GB/T 708 Dimension, Shape, Weight and Tolerance for Cold-rolled Steel Strip and Sheet
GB/T 2523 Measuring Method of Surface Roughness, Peak Count and Waviness for Cold-
rolled Metal Sheet and Strip
GB/T 2975 Steel and Steel Products - Location and Preparation of Samples and Test Pieces for
Mechanical Testing
GB/T 4336 Carbon and Low-alloy Steel - Determination of Multi-element Contents - Spark
Discharge Atomic Emission Spectrometric Method (routine method)
GB/T 5028 Metallic Materials - Sheet and Strip - Determination of Tensile Strain Hardening
Exponent
GB/T 8170 Rules of Rounding off for Numerical Values and Expression and Judgement of
Limiting Values
GB/T 17505 Steel and Steel Products - General Technical Delivery Requirements
GB/T 18253-2018 Steel and Steel Products - Types of Inspection Documents
GB/T 20066 Steel and Iron - Sampling and Preparation of Samples for the Determination of
Chemical Composition
GB/T 20123 Steel and Iron - Determination of Total Carbon and Sulfur Content Infrared
Absorption Method after Combustion in an Induction Furnace (routine method)
GB/T 20125 Low-alloy Steel - Determination of Multi-element Contents - Inductively Coupled
Plasma Atomic Emission Spectrometric Method
3 Terms and Definitions
The following terms and definitions are applicable to this document.
3.1 Transformation Induced Plasticity Steel; TR
Transformation induced plasticity steel refers to a type of steel whose microstructure is mainly
ferrite, bainite and retained austenite, and during the forming process, the retained austenite
may be transformed into a martensitic structure.
NOTE. transformation induced plasticity steel has a relatively high work hardening rate, uniform
elongation and tensile strength. In comparison with dual phase steel with equivalent tensile
strength, transformation induced plasticity steel has a higher elongation.
4 Classification and Designation Expression Method
4.1 Designation Expression Method
The designation of the steel sheet and strip is composed of three parts. the initials “CR” of the
English “Cold Rolled”, the specified minimum yield strength value / specified minimum tensile
strength value, and the first two letters “TR” of the English “Transformation Induced Plasticity”.
Example. CR380/590TR, in which.
CR---the initials of the English “Cold Rolled”;
380/590---380.the specified minimum yield strength value, 590.the specified minimum tensile strength
value, expressed in (MPa);
TR---the first two letters of the English “Transformation Induced Plasticity”.
4.2 Classification
4.2.1 The designations and recommended purposes of the steel sheet and strip are shown in
Table 1.
d) Specifications, dimensions and unevenness accuracy;
e) Surface quality level;
f) Surface structure;
g) Edge state;
h) Packaging mode;
i) Weight;
j) Purposes;
k) Other special requirements.
5.2 If the dimensions, unevenness accuracy, surface quality level, surface structure type, edge
state and packaging are not specified in the order contract, then, the products in this document
shall be delivered with ordinary dimensions and unevenness accuracy, and a relatively advanced
surface as tr...
Share